人造石岗石用不饱和聚酯树脂
LY-288H
产品名称: | LY-288H |
外观/Appearance: | 浅黄透明液体 |
粘度/Viscosity(25℃ mPa.s): | 900±100 |
胶凝时间/Gel time(25℃ min): | 22.5±2.5 |
固体含量/Non-Volatile %: | 70.0±3.0 |
巴氏硬度≥: | 28 |
弯曲强度Mpa≥: | 60 |
弯曲弹性模量MPa×104≥: | 1.5 |
LY-288H-2
产品名称: | LY-288H-2 |
外观/Appearance: | 浅黄透明液体 |
粘度/Viscosity(25℃ mPa.s): | 900±100 |
胶凝时间/Gel time(25℃ min): | 33.5±3.5 |
固体含量/Non-Volatile %: | 69.5±1.5 |
巴氏硬度≥: | 30 |
弯曲强度Mpa≥: | 60 |
弯曲弹性模量MPa×104≥: | 2.0 |
LY-288K
产品名称: | LY-288K |
特点: | 硬度高、浸润性好、强度高、耐腐蚀性,适用于人造岗石制品。 |
外观/Appearance: | 浅黄透明液体 |
粘度/Viscosity(25℃ mPa.s): | 800±100 |
胶凝时间/Gel time(25℃ min): | 12.5±2.5 |
固体含量/Non-Volatile %: | 69.0±3.0 |
巴氏硬度≥: | 30 |
弯曲强度Mpa≥: | 80 |
弯曲弹性模量MPa×104≥: | 2.5 |
LY-288Q
产品名称: | LY-288Q |
外观/Appearance: | 黄绿透明液体 |
粘度/Viscosity(25℃ mPa.s): | 900±100 |
胶凝时间/Gel time(25℃ min): | 33.5±3.5 |
固体含量/Non-Volatile %: | 70.5±1.5 |
巴氏硬度≥: | 28 |
弯曲强度Mpa≥: | 90 |
弯曲弹性模量MPa×104≥: | 2.0 |
LY-7417
产品名称: | LY-7417 |
外观/Appearance: | 浅黄透明液体 |
粘度/Viscosity(25℃ mPa.s): | 900±100 |
胶凝时间/Gel time(25℃ min): | 25.5±2.5 |
固体含量/Non-Volatile %: | 68.0±3.0 |
巴氏硬度≥: | 32 |
弯曲强度Mpa≥: | 80 |
弯曲弹性模量MPa×104≥: | 2.0 |
LY-FA404
产品名称: | LY-FA404 |
外观/Appearance: | 浅青透明液体 |
粘度/Viscosity(25℃ mPa.s): | 550±50 |
胶凝时间/Gel time(25℃ min): | 25.5±2.5 |
固体含量/Non-Volatile %: | 65.0±3.0 |
巴氏硬度≥: | 20 |
弯曲强度Mpa≥: | 60 |
弯曲弹性模量MPa×104≥: | 2.0 |
LY-FA406
产品名称: | LY-FA406 |
外观/Appearance: | 黄色透明液体 |
粘度/Viscosity(25℃ mPa.s): | 750±50 |
胶凝时间/Gel time(25℃ min): | 19.5±2.5 |
固体含量/Non-Volatile %: | 73.0±2.0 |
巴氏硬度≥: | 20 |
弯曲强度Mpa≥: | 60 |
弯曲弹性模量MPa×104≥: | 2.0 |
LY-FA409
产品名称: | LY-FA409 |
外观/Appearance: | 黄色到黄绿透明液体 |
粘度/Viscosity(25℃ mPa.s): | 700±50 |
胶凝时间/Gel time(25℃ min): | 22.5±2.5 |
固体含量/Non-Volatile %: | 70.0±3.0 |
巴氏硬度≥: | 20 |
弯曲强度Mpa≥: | 70 |
弯曲弹性模量MPa×104≥: | 2.5 |